N06045 Nickel vs. C42500 Brass
N06045 nickel belongs to the nickel alloys classification, while C42500 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is N06045 nickel and the bottom bar is C42500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 37 | |
| 2.0 to 49 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 42 |
| Shear Strength, MPa | 470 | |
| 220 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 310 to 630 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 120 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 1010 | |
| 180 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1030 |
| Melting Onset (Solidus), °C | 1300 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 42 | |
| 30 |
| Density, g/cm3 | 8.0 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 6.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 98 | |
| 46 |
| Embodied Water, L/kg | 250 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 12 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 64 to 1570 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 24 | |
| 9.9 to 20 |
| Strength to Weight: Bending, points | 22 | |
| 12 to 19 |
| Thermal Shock Resistance, points | 18 | |
| 11 to 22 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.12 | |
| 0 |
| Cerium (Ce), % | 0.030 to 0.090 | |
| 0 |
| Chromium (Cr), % | 26 to 29 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 87 to 90 |
| Iron (Fe), % | 21 to 25 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 45 to 50.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.35 |
| Silicon (Si), % | 2.5 to 3.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 3.0 |
| Zinc (Zn), % | 0 | |
| 6.1 to 11.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |