N06045 Nickel vs. C83800 Bronze

N06045 nickel belongs to the nickel alloys classification, while C83800 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N06045 nickel and the bottom bar is C83800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 37
20
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
39
Tensile Strength: Ultimate (UTS), MPa 690
230
Tensile Strength: Yield (Proof), MPa 270
110

Thermal Properties

Latent Heat of Fusion, J/g 350
180
Maximum Temperature: Mechanical, °C 1010
160
Melting Completion (Liquidus), °C 1350
1000
Melting Onset (Solidus), °C 1300
840
Specific Heat Capacity, J/kg-K 480
370
Thermal Expansion, µm/m-K 13
19

Otherwise Unclassified Properties

Base Metal Price, % relative 42
30
Density, g/cm3 8.0
8.8
Embodied Carbon, kg CO2/kg material 6.9
2.9
Embodied Energy, MJ/kg 98
47
Embodied Water, L/kg 250
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
39
Resilience: Unit (Modulus of Resilience), kJ/m3 180
53
Stiffness to Weight: Axial, points 14
6.6
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 24
7.4
Strength to Weight: Bending, points 22
9.6
Thermal Shock Resistance, points 18
8.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0.050 to 0.12
0
Cerium (Ce), % 0.030 to 0.090
0
Chromium (Cr), % 26 to 29
0
Copper (Cu), % 0 to 0.3
82 to 83.8
Iron (Fe), % 21 to 25
0 to 0.3
Lead (Pb), % 0
5.0 to 7.0
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 45 to 50.4
0 to 1.0
Phosphorus (P), % 0 to 0.020
0 to 1.5
Silicon (Si), % 2.5 to 3.0
0 to 0.0050
Sulfur (S), % 0 to 0.010
0 to 0.080
Tin (Sn), % 0
3.3 to 4.2
Zinc (Zn), % 0
5.0 to 8.0
Residuals, % 0
0 to 0.7