N06058 Nickel vs. 60Pd-40Ag Alloy
N06058 nickel belongs to the nickel alloys classification, while 60Pd-40Ag alloy belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N06058 nickel and the bottom bar is 60Pd-40Ag alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 100 |
| Elongation at Break, % | 45 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.29 | |
| 0.38 |
| Shear Modulus, GPa | 86 | |
| 37 |
| Shear Strength, MPa | 600 | |
| 220 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 340 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 140 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1360 |
| Melting Onset (Solidus), °C | 1490 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 240 |
| Thermal Conductivity, W/m-K | 9.8 | |
| 29 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 4.9 |
| Stiffness to Weight: Bending, points | 23 | |
| 14 |
| Strength to Weight: Axial, points | 27 | |
| 8.4 to 18 |
| Strength to Weight: Bending, points | 23 | |
| 9.6 to 16 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 11 |
| Thermal Shock Resistance, points | 23 | |
| 16 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Chromium (Cr), % | 20 to 23 | |
| 0 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 19 to 21 | |
| 0 |
| Nickel (Ni), % | 52.2 to 61 | |
| 0 |
| Nitrogen (N), % | 0.020 to 0.15 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 59.5 to 60.9 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Silver (Ag), % | 0 | |
| 39.1 to 40.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |