N06058 Nickel vs. AWS E430Nb
N06058 nickel belongs to the nickel alloys classification, while AWS E430Nb belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is N06058 nickel and the bottom bar is AWS E430Nb.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 45 | |
| 23 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 86 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1450 |
| Melting Onset (Solidus), °C | 1490 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Conductivity, W/m-K | 9.8 | |
| 24 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 15 |
| Density, g/cm3 | 8.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 3.1 |
| Embodied Energy, MJ/kg | 170 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 27 | |
| 18 |
| Strength to Weight: Bending, points | 23 | |
| 18 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 6.6 |
| Thermal Shock Resistance, points | 23 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.1 |
| Chromium (Cr), % | 20 to 23 | |
| 15 to 18 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 to 1.5 | |
| 76.2 to 84.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 19 to 21 | |
| 0 to 0.75 |
| Nickel (Ni), % | 52.2 to 61 | |
| 0 to 0.6 |
| Niobium (Nb), % | 0 | |
| 0.5 to 1.5 |
| Nitrogen (N), % | 0.020 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 to 0.3 | |
| 0 |