N06058 Nickel vs. SAE-AISI 1527 Steel

N06058 nickel belongs to the nickel alloys classification, while SAE-AISI 1527 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N06058 nickel and the bottom bar is SAE-AISI 1527 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 45
13 to 21
Fatigue Strength, MPa 350
220 to 350
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Shear Strength, MPa 600
370 to 390
Tensile Strength: Ultimate (UTS), MPa 860
590 to 640
Tensile Strength: Yield (Proof), MPa 410
320 to 550

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1540
1460
Melting Onset (Solidus), °C 1490
1420
Specific Heat Capacity, J/kg-K 420
470
Thermal Conductivity, W/m-K 9.8
52
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 70
1.8
Density, g/cm3 8.8
7.8
Embodied Carbon, kg CO2/kg material 13
1.4
Embodied Energy, MJ/kg 170
19
Embodied Water, L/kg 310
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
82 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 370
260 to 800
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 27
21 to 23
Strength to Weight: Bending, points 23
20 to 21
Thermal Diffusivity, mm2/s 2.6
14
Thermal Shock Resistance, points 23
19 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.4
0
Carbon (C), % 0 to 0.010
0.22 to 0.29
Chromium (Cr), % 20 to 23
0
Cobalt (Co), % 0 to 0.3
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 1.5
98.1 to 98.6
Manganese (Mn), % 0 to 0.5
1.2 to 1.5
Molybdenum (Mo), % 19 to 21
0
Nickel (Ni), % 52.2 to 61
0
Nitrogen (N), % 0.020 to 0.15
0
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0 to 0.1
0
Sulfur (S), % 0 to 0.010
0 to 0.050
Tungsten (W), % 0 to 0.3
0