N06058 Nickel vs. SAE-AISI 5130 Steel
N06058 nickel belongs to the nickel alloys classification, while SAE-AISI 5130 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is N06058 nickel and the bottom bar is SAE-AISI 5130 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 | |
190 |
Elongation at Break, % | 45 | |
12 to 22 |
Fatigue Strength, MPa | 350 | |
230 to 330 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 86 | |
73 |
Shear Strength, MPa | 600 | |
310 to 390 |
Tensile Strength: Ultimate (UTS), MPa | 860 | |
500 to 640 |
Tensile Strength: Yield (Proof), MPa | 410 | |
330 to 530 |
Thermal Properties
Latent Heat of Fusion, J/g | 330 | |
250 |
Maximum Temperature: Mechanical, °C | 980 | |
420 |
Melting Completion (Liquidus), °C | 1540 | |
1460 |
Melting Onset (Solidus), °C | 1490 | |
1420 |
Specific Heat Capacity, J/kg-K | 420 | |
470 |
Thermal Conductivity, W/m-K | 9.8 | |
45 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 70 | |
2.2 |
Density, g/cm3 | 8.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 13 | |
1.4 |
Embodied Energy, MJ/kg | 170 | |
19 |
Embodied Water, L/kg | 310 | |
50 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
74 to 98 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
290 to 750 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 23 | |
24 |
Strength to Weight: Axial, points | 27 | |
18 to 23 |
Strength to Weight: Bending, points | 23 | |
18 to 21 |
Thermal Diffusivity, mm2/s | 2.6 | |
12 |
Thermal Shock Resistance, points | 23 | |
16 to 20 |
Alloy Composition
Aluminum (Al), % | 0 to 0.4 | |
0 |
Carbon (C), % | 0 to 0.010 | |
0.28 to 0.33 |
Chromium (Cr), % | 20 to 23 | |
0.8 to 1.1 |
Cobalt (Co), % | 0 to 0.3 | |
0 |
Copper (Cu), % | 0 to 0.5 | |
0 |
Iron (Fe), % | 0 to 1.5 | |
97.2 to 98.1 |
Manganese (Mn), % | 0 to 0.5 | |
0.7 to 0.9 |
Molybdenum (Mo), % | 19 to 21 | |
0 |
Nickel (Ni), % | 52.2 to 61 | |
0 |
Nitrogen (N), % | 0.020 to 0.15 | |
0 |
Phosphorus (P), % | 0 to 0.015 | |
0 to 0.035 |
Silicon (Si), % | 0 to 0.1 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.010 | |
0 to 0.040 |
Tungsten (W), % | 0 to 0.3 | |
0 |