N06058 Nickel vs. SAE-AISI D5 Steel

N06058 nickel belongs to the nickel alloys classification, while SAE-AISI D5 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N06058 nickel and the bottom bar is SAE-AISI D5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 45
5.4 to 14
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 86
75
Shear Strength, MPa 600
470 to 1180
Tensile Strength: Ultimate (UTS), MPa 860
770 to 2030

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1540
1430
Melting Onset (Solidus), °C 1490
1390
Specific Heat Capacity, J/kg-K 420
480
Thermal Conductivity, W/m-K 9.8
27
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 70
13
Density, g/cm3 8.8
7.7
Embodied Carbon, kg CO2/kg material 13
3.5
Embodied Energy, MJ/kg 170
51
Embodied Water, L/kg 310
120

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 27
28 to 73
Strength to Weight: Bending, points 23
24 to 46
Thermal Diffusivity, mm2/s 2.6
7.4
Thermal Shock Resistance, points 23
26 to 67

Alloy Composition

Aluminum (Al), % 0 to 0.4
0
Carbon (C), % 0 to 0.010
1.4 to 1.6
Chromium (Cr), % 20 to 23
11 to 13
Cobalt (Co), % 0 to 0.3
2.5 to 3.5
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 1.5
77.9 to 84.4
Manganese (Mn), % 0 to 0.5
0 to 0.6
Molybdenum (Mo), % 19 to 21
0.7 to 1.2
Nickel (Ni), % 52.2 to 61
0 to 0.3
Nitrogen (N), % 0.020 to 0.15
0
Phosphorus (P), % 0 to 0.015
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.030
Tungsten (W), % 0 to 0.3
0
Vanadium (V), % 0
0 to 1.0