N06060 Nickel vs. AISI W1 Steel
N06060 nickel belongs to the nickel alloys classification, while AISI W1 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is N06060 nickel and the bottom bar is AISI W1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 82 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 700 | |
| 590 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Melting Completion (Liquidus), °C | 1510 | |
| 1450 |
| Melting Onset (Solidus), °C | 1450 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 2.2 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 1.6 |
| Embodied Energy, MJ/kg | 160 | |
| 21 |
| Embodied Water, L/kg | 280 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 21 to 83 |
| Strength to Weight: Bending, points | 20 | |
| 20 to 50 |
| Thermal Shock Resistance, points | 19 | |
| 22 to 85 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.7 to 1.5 |
| Chromium (Cr), % | 19 to 22 | |
| 0 to 0.15 |
| Copper (Cu), % | 0.25 to 1.3 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 14 | |
| 96.4 to 98.9 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.35 to 0.73 |
| Molybdenum (Mo), % | 12 to 14 | |
| 0 to 0.1 |
| Nickel (Ni), % | 54 to 60 | |
| 0 to 0.2 |
| Niobium (Nb), % | 0.5 to 1.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.025 |
| Tungsten (W), % | 0.25 to 1.3 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |