N06060 Nickel vs. ASTM B563 Pd-Ag-Cu

N06060 nickel belongs to the nickel alloys classification, while ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06060 nickel and the bottom bar is ASTM B563 Pd-Ag-Cu.

UNS N06060 Nickel Alloy ASTM B563 Palladium-Silver-Copper Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		100

Elongation at Break, %		45
Elongation at Break, %		7.0 to 17

Poisson's Ratio		0.29
Poisson's Ratio		0.37

Shear Modulus, GPa		82
Shear Modulus, GPa		37

Shear Strength, MPa		490
Shear Strength, MPa		470 to 690

Tensile Strength: Ultimate (UTS), MPa		700
Tensile Strength: Ultimate (UTS), MPa		760 to 1170

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		150

Melting Completion (Liquidus), °C		1510
Melting Completion (Liquidus), °C		1180

Melting Onset (Solidus), °C		1450
Melting Onset (Solidus), °C		1030

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		260

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Density, g/cm³		8.7
Density, g/cm³		11

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		5.2

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		19 to 30

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		17 to 22

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		39 to 61

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0

Chromium (Cr), %		19 to 22
Chromium (Cr), %		0

Copper (Cu), %		0.25 to 1.3
Copper (Cu), %		15.5 to 16.5

Iron (Fe), %		0 to 14
Iron (Fe), %		0

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		0

Molybdenum (Mo), %		12 to 14
Molybdenum (Mo), %		0

Nickel (Ni), %		54 to 60
Nickel (Ni), %		0.8 to 1.2

Niobium (Nb), %		0.5 to 1.3
Niobium (Nb), %		0

Palladium (Pd), %		0
Palladium (Pd), %		43 to 45

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0

Platinum (Pt), %		0
Platinum (Pt), %		0.8 to 1.2

Silicon (Si), %		0 to 0.5
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		37 to 39

Sulfur (S), %		0 to 0.0050
Sulfur (S), %		0

Tungsten (W), %		0.25 to 1.3
Tungsten (W), %		0

Residuals, %		0
Residuals, %		0 to 0.4