N06060 Nickel vs. AWS E309LMo

N06060 nickel belongs to the nickel alloys classification, while AWS E309LMo belongs to the iron alloys. They have 44% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N06060 nickel and the bottom bar is AWS E309LMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 45
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 82
79
Tensile Strength: Ultimate (UTS), MPa 700
580

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Melting Completion (Liquidus), °C 1510
1430
Melting Onset (Solidus), °C 1450
1390
Specific Heat Capacity, J/kg-K 430
480
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 65
22
Density, g/cm3 8.7
7.9
Embodied Carbon, kg CO2/kg material 12
4.2
Embodied Energy, MJ/kg 160
59
Embodied Water, L/kg 280
180

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 20
20
Thermal Shock Resistance, points 19
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.040
Chromium (Cr), % 19 to 22
22 to 25
Copper (Cu), % 0.25 to 1.3
0 to 0.75
Iron (Fe), % 0 to 14
53.6 to 63.5
Manganese (Mn), % 0 to 1.5
0.5 to 2.5
Molybdenum (Mo), % 12 to 14
2.0 to 3.0
Nickel (Ni), % 54 to 60
12 to 14
Niobium (Nb), % 0.5 to 1.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.030
Tungsten (W), % 0.25 to 1.3
0