N06060 Nickel vs. SAE-AISI H22 Steel

N06060 nickel belongs to the nickel alloys classification, while SAE-AISI H22 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N06060 nickel and the bottom bar is SAE-AISI H22 steel.

UNS N06060 Nickel Alloy SAE-AISI H22 (T20822) Tungsten Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		82
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		700
Tensile Strength: Ultimate (UTS), MPa		700 to 1920

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1510
Melting Completion (Liquidus), °C		1670

Melting Onset (Solidus), °C		1450
Melting Onset (Solidus), °C		1620

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		65
Base Metal Price, % relative		28

Density, g/cm³		8.7
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		4.9

Embodied Energy, MJ/kg		160
Embodied Energy, MJ/kg		73

Embodied Water, L/kg		280
Embodied Water, L/kg		72

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		22 to 61

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		20 to 39

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		22 to 60

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0.3 to 0.4

Chromium (Cr), %		19 to 22
Chromium (Cr), %		1.8 to 3.8

Copper (Cu), %		0.25 to 1.3
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 14
Iron (Fe), %		82.2 to 87.4

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		12 to 14
Molybdenum (Mo), %		0

Nickel (Ni), %		54 to 60
Nickel (Ni), %		0 to 0.3

Niobium (Nb), %		0.5 to 1.3
Niobium (Nb), %		0

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.5
Silicon (Si), %		0.15 to 0.4

Sulfur (S), %		0 to 0.0050
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0.25 to 1.3
Tungsten (W), %		10 to 11.8

Vanadium (V), %		0
Vanadium (V), %		0.25 to 0.5