N06110 Nickel vs. AISI 410Cb Stainless Steel
N06110 nickel belongs to the nickel alloys classification, while AISI 410Cb stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is N06110 nickel and the bottom bar is AISI 410Cb stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 53 | |
| 15 |
| Fatigue Strength, MPa | 320 | |
| 180 to 460 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 84 | |
| 76 |
| Shear Strength, MPa | 530 | |
| 340 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 550 to 960 |
| Tensile Strength: Yield (Proof), MPa | 330 | |
| 310 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 1020 | |
| 730 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1450 |
| Melting Onset (Solidus), °C | 1440 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 7.5 |
| Density, g/cm3 | 8.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.0 |
| Embodied Energy, MJ/kg | 160 | |
| 29 |
| Embodied Water, L/kg | 320 | |
| 97 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 70 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 240 to 1600 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 20 to 35 |
| Strength to Weight: Bending, points | 21 | |
| 19 to 28 |
| Thermal Shock Resistance, points | 20 | |
| 20 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.0 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.18 |
| Chromium (Cr), % | 28 to 33 | |
| 11 to 13 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 84.5 to 89 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 9.0 to 12 | |
| 0 |
| Nickel (Ni), % | 51 to 62 | |
| 0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0.050 to 0.3 |
| Phosphorus (P), % | 0 to 0.5 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 1.0 to 4.0 | |
| 0 |