N06110 Nickel vs. AWS E110C-K4
N06110 nickel belongs to the nickel alloys classification, while AWS E110C-K4 belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is N06110 nickel and the bottom bar is AWS E110C-K4.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 53 | |
| 17 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 850 |
| Tensile Strength: Yield (Proof), MPa | 330 | |
| 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 250 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1460 |
| Melting Onset (Solidus), °C | 1440 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 3.5 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 1.7 |
| Embodied Energy, MJ/kg | 160 | |
| 23 |
| Embodied Water, L/kg | 320 | |
| 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 1600 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 23 | |
| 30 |
| Strength to Weight: Bending, points | 21 | |
| 25 |
| Thermal Shock Resistance, points | 20 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.0 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.15 |
| Chromium (Cr), % | 28 to 33 | |
| 0.15 to 0.65 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.35 |
| Iron (Fe), % | 0 to 1.0 | |
| 92.1 to 98.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.75 to 2.3 |
| Molybdenum (Mo), % | 9.0 to 12 | |
| 0.25 to 0.65 |
| Nickel (Ni), % | 51 to 62 | |
| 0.5 to 2.5 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.5 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 1.0 to 4.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 | |
| 0 to 0.5 |