N06110 Nickel vs. CC764S Brass
N06110 nickel belongs to the nickel alloys classification, while CC764S brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is N06110 nickel and the bottom bar is CC764S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 53 | |
| 15 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 84 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 680 |
| Tensile Strength: Yield (Proof), MPa | 330 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 1020 | |
| 130 |
| Melting Completion (Liquidus), °C | 1490 | |
| 850 |
| Melting Onset (Solidus), °C | 1440 | |
| 810 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 400 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 23 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.9 |
| Embodied Energy, MJ/kg | 160 | |
| 49 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 390 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 23 | |
| 20 |
| Strength to Weight: Axial, points | 23 | |
| 24 |
| Strength to Weight: Bending, points | 21 | |
| 22 |
| Thermal Shock Resistance, points | 20 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.0 | |
| 1.0 to 3.0 |
| Antimony (Sb), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 28 to 33 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 52 to 66 |
| Iron (Fe), % | 0 to 1.0 | |
| 0.5 to 2.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 4.0 |
| Molybdenum (Mo), % | 9.0 to 12 | |
| 0 |
| Nickel (Ni), % | 51 to 62 | |
| 0 to 3.0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.5 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 1.0 to 4.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 20.7 to 50.2 |