N06110 Nickel vs. Solder Alloy 151

N06110 nickel belongs to the nickel alloys classification, while solder alloy 151 belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N06110 nickel and the bottom bar is solder alloy 151.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
39
Elongation at Break, % 53
37
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 84
14
Tensile Strength: Ultimate (UTS), MPa 730
46

Thermal Properties

Latent Heat of Fusion, J/g 340
47
Melting Completion (Liquidus), °C 1490
150
Melting Onset (Solidus), °C 1440
150
Specific Heat Capacity, J/kg-K 440
190
Thermal Expansion, µm/m-K 12
26

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.8
Embodied Carbon, kg CO2/kg material 11
9.2
Embodied Energy, MJ/kg 160
160
Embodied Water, L/kg 320
920

Common Calculations

Stiffness to Weight: Axial, points 14
2.5
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 23
1.4
Strength to Weight: Bending, points 21
3.2
Thermal Shock Resistance, points 20
3.2

Alloy Composition

Aluminum (Al), % 0 to 1.0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
17.5 to 18.5
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 28 to 33
0
Copper (Cu), % 0 to 0.5
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 1.0
0 to 0.020
Lead (Pb), % 0
30.3 to 33
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 9.0 to 12
0
Nickel (Ni), % 51 to 62
0 to 0.010
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.5
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
49.5 to 50.5
Titanium (Ti), % 0 to 1.0
0
Tungsten (W), % 1.0 to 4.0
0
Zinc (Zn), % 0
0 to 0.0010