N06110 Nickel vs. Solder Alloy 182

N06110 nickel belongs to the nickel alloys classification, while solder alloy 182 belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06110 nickel and the bottom bar is solder alloy 182.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
19
Elongation at Break, % 53
37
Poisson's Ratio 0.28
0.44
Shear Modulus, GPa 84
6.7
Tensile Strength: Ultimate (UTS), MPa 730
28

Thermal Properties

Latent Heat of Fusion, J/g 340
28
Melting Completion (Liquidus), °C 1490
370
Melting Onset (Solidus), °C 1440
300
Specific Heat Capacity, J/kg-K 440
130
Thermal Expansion, µm/m-K 12
29

Otherwise Unclassified Properties

Density, g/cm3 8.6
11
Embodied Carbon, kg CO2/kg material 11
9.0
Embodied Energy, MJ/kg 160
140

Common Calculations

Stiffness to Weight: Axial, points 14
0.95
Stiffness to Weight: Bending, points 23
7.9
Strength to Weight: Axial, points 23
0.69
Strength to Weight: Bending, points 21
1.8
Thermal Shock Resistance, points 20
3.7

Alloy Composition

Aluminum (Al), % 0 to 1.0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 28 to 33
0
Copper (Cu), % 0 to 0.5
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 1.0
0 to 0.020
Lead (Pb), % 0
93.2 to 95
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 9.0 to 12
0
Nickel (Ni), % 51 to 62
0 to 0.010
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.5
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
5.0 to 6.0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.25
Titanium (Ti), % 0 to 1.0
0
Tungsten (W), % 1.0 to 4.0
0
Zinc (Zn), % 0
0 to 0.0010