N06110 Nickel vs. Nickel 59
Both N06110 nickel and nickel 59 are nickel alloys. Both are furnished in the annealed condition. They have a moderately high 91% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is N06110 nickel and the bottom bar is nickel 59.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 220 |
| Elongation at Break, % | 53 | |
| 50 |
| Fatigue Strength, MPa | 320 | |
| 320 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 84 |
| Shear Strength, MPa | 530 | |
| 560 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 780 |
| Tensile Strength: Yield (Proof), MPa | 330 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 1020 | |
| 990 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1500 |
| Melting Onset (Solidus), °C | 1440 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 430 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 65 |
| Density, g/cm3 | 8.6 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 12 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 23 | |
| 25 |
| Strength to Weight: Bending, points | 21 | |
| 22 |
| Thermal Shock Resistance, points | 20 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.0 | |
| 0.1 to 0.4 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.010 |
| Chromium (Cr), % | 28 to 33 | |
| 22 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 1.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 9.0 to 12 | |
| 15 to 16.5 |
| Nickel (Ni), % | 51 to 62 | |
| 56.2 to 62.9 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.5 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |
| Tungsten (W), % | 1.0 to 4.0 | |
| 0 |