N06210 Nickel vs. EN 1.0420 Cast Steel

N06210 nickel belongs to the nickel alloys classification, while EN 1.0420 cast steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N06210 nickel and the bottom bar is EN 1.0420 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 51
28
Fatigue Strength, MPa 320
170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 85
73
Tensile Strength: Ultimate (UTS), MPa 780
460
Tensile Strength: Yield (Proof), MPa 350
220

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1570
1470
Melting Onset (Solidus), °C 1510
1430
Specific Heat Capacity, J/kg-K 420
470
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 85
1.7
Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 17
1.4
Embodied Energy, MJ/kg 250
18
Embodied Water, L/kg 310
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
110
Resilience: Unit (Modulus of Resilience), kJ/m3 280
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 24
16
Strength to Weight: Bending, points 21
17
Thermal Shock Resistance, points 22
14

Alloy Composition

Carbon (C), % 0 to 0.015
0
Chromium (Cr), % 18 to 20
0
Cobalt (Co), % 0 to 1.0
0
Iron (Fe), % 0 to 1.0
99.935 to 100
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 18 to 20
0
Nickel (Ni), % 54.8 to 62.5
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.080
0
Sulfur (S), % 0 to 0.020
0 to 0.030
Tantalum (Ta), % 1.5 to 2.2
0
Vanadium (V), % 0 to 0.35
0