N06210 Nickel vs. Grade TDSiCrV Steel
N06210 nickel belongs to the nickel alloys classification, while grade TDSiCrV steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N06210 nickel and the bottom bar is grade TDSiCrV steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 85 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 2100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 420 |
| Melting Completion (Liquidus), °C | 1570 | |
| 1440 |
| Melting Onset (Solidus), °C | 1510 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 85 | |
| 2.3 |
| Density, g/cm3 | 9.0 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 17 | |
| 1.9 |
| Embodied Energy, MJ/kg | 250 | |
| 26 |
| Embodied Water, L/kg | 310 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 75 |
| Strength to Weight: Bending, points | 21 | |
| 47 |
| Thermal Shock Resistance, points | 22 | |
| 63 |
Alloy Composition
| Carbon (C), % | 0 to 0.015 | |
| 0.5 to 0.7 |
| Chromium (Cr), % | 18 to 20 | |
| 0.5 to 1.0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.0 | |
| 96.1 to 97.8 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 18 to 20 | |
| 0 |
| Nickel (Ni), % | 54.8 to 62.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.080 | |
| 1.2 to 1.7 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Tantalum (Ta), % | 1.5 to 2.2 | |
| 0 |
| Vanadium (V), % | 0 to 0.35 | |
| 0.1 to 0.25 |