N06230 Nickel vs. ASTM A216 Cast Steel
N06230 nickel belongs to the nickel alloys classification, while ASTM A216 cast steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is N06230 nickel and the bottom bar is ASTM A216 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 38 to 48 | |
| 25 to 27 |
| Fatigue Strength, MPa | 250 to 360 | |
| 170 to 230 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 840 | |
| 500 to 570 |
| Tensile Strength: Yield (Proof), MPa | 330 to 400 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 400 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 1300 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Conductivity, W/m-K | 8.9 | |
| 49 to 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 7.1 to 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.3 | |
| 8.2 to 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 85 | |
| 1.8 |
| Density, g/cm3 | 9.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 1.4 |
| Embodied Energy, MJ/kg | 160 | |
| 18 |
| Embodied Water, L/kg | 290 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 330 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 380 | |
| 140 to 250 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 25 | |
| 18 to 20 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 2.3 | |
| 13 to 14 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 16 to 18 |