N06230 Nickel vs. ASTM B541 Gold
N06230 nickel belongs to the nickel alloys classification, while ASTM B541 gold belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is N06230 nickel and the bottom bar is ASTM B541 gold.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 38 to 48 | |
| 6.0 to 14 |
| Poisson's Ratio | 0.28 | |
| 0.4 |
| Shear Modulus, GPa | 83 | |
| 38 |
| Shear Strength, MPa | 420 to 600 | |
| 410 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 840 | |
| 670 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 330 to 400 | |
| 480 to 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 90 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1110 |
| Melting Onset (Solidus), °C | 1300 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 170 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 7.7 to 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.3 | |
| 4.0 to 6.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.5 | |
| 17 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 330 | |
| 65 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 380 | |
| 1090 to 3830 |
| Stiffness to Weight: Axial, points | 12 | |
| 3.4 |
| Stiffness to Weight: Bending, points | 21 | |
| 9.0 |
| Strength to Weight: Axial, points | 18 to 25 | |
| 11 to 19 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 9.8 to 14 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 36 to 63 |
Alloy Composition
| Aluminum (Al), % | 0.2 to 0.5 | |
| 0 |
| Boron (B), % | 0 to 0.015 | |
| 0 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 |
| Chromium (Cr), % | 20 to 24 | |
| 0 |
| Cobalt (Co), % | 0 to 5.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 13.5 to 15.5 |
| Gold (Au), % | 0 | |
| 70.5 to 72.5 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 |
| Lanthanum (La), % | 0.0050 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0.3 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 1.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 47.5 to 65.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 8.0 to 9.0 |
| Silicon (Si), % | 0.25 to 0.75 | |
| 0 |
| Silver (Ag), % | 0 | |
| 4.0 to 5.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tungsten (W), % | 13 to 15 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0.7 to 1.3 |
| Residuals, % | 0 | |
| 0 to 0.4 |