N06230 Nickel vs. EN 1.4923 Stainless Steel

N06230 nickel belongs to the nickel alloys classification, while EN 1.4923 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N06230 nickel and the bottom bar is EN 1.4923 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 38 to 48
12 to 21
Fatigue Strength, MPa 250 to 360
300 to 440
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 83
76
Shear Strength, MPa 420 to 600
540 to 590
Tensile Strength: Ultimate (UTS), MPa 620 to 840
870 to 980
Tensile Strength: Yield (Proof), MPa 330 to 400
470 to 780

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Mechanical, °C 990
740
Melting Completion (Liquidus), °C 1370
1450
Melting Onset (Solidus), °C 1300
1410
Specific Heat Capacity, J/kg-K 420
480
Thermal Conductivity, W/m-K 8.9
24
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 85
8.0
Density, g/cm3 9.5
7.8
Embodied Carbon, kg CO2/kg material 11
2.9
Embodied Energy, MJ/kg 160
41
Embodied Water, L/kg 290
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 330
110 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 380
570 to 1580
Stiffness to Weight: Axial, points 12
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 18 to 25
31 to 35
Strength to Weight: Bending, points 17 to 21
26 to 28
Thermal Diffusivity, mm2/s 2.3
6.5
Thermal Shock Resistance, points 17 to 23
30 to 34

Alloy Composition

Aluminum (Al), % 0.2 to 0.5
0
Boron (B), % 0 to 0.015
0
Carbon (C), % 0.050 to 0.15
0.18 to 0.24
Chromium (Cr), % 20 to 24
11 to 12.5
Cobalt (Co), % 0 to 5.0
0
Iron (Fe), % 0 to 3.0
83.5 to 87.1
Lanthanum (La), % 0.0050 to 0.050
0
Manganese (Mn), % 0.3 to 1.0
0.4 to 0.9
Molybdenum (Mo), % 1.0 to 3.0
0.8 to 1.2
Nickel (Ni), % 47.5 to 65.2
0.3 to 0.8
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.25 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015
Tungsten (W), % 13 to 15
0
Vanadium (V), % 0
0.25 to 0.35

Comparable Variants