N06230 Nickel vs. Solder Alloy 135
N06230 nickel belongs to the nickel alloys classification, while solder alloy 135 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N06230 nickel and the bottom bar is solder alloy 135.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 27 |
| Elongation at Break, % | 38 to 48 | |
| 20 |
| Poisson's Ratio | 0.28 | |
| 0.41 |
| Shear Modulus, GPa | 83 | |
| 9.5 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 840 | |
| 35 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 36 |
| Melting Completion (Liquidus), °C | 1370 | |
| 250 |
| Melting Onset (Solidus), °C | 1300 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 160 |
| Thermal Conductivity, W/m-K | 8.9 | |
| 42 |
| Thermal Expansion, µm/m-K | 13 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 9.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.3 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 85 | |
| 90 |
| Density, g/cm3 | 9.5 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 7.3 |
| Embodied Energy, MJ/kg | 160 | |
| 120 |
| Embodied Water, L/kg | 290 | |
| 720 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 21 | |
| 9.9 |
| Strength to Weight: Axial, points | 18 to 25 | |
| 1.0 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 2.4 |
| Thermal Diffusivity, mm2/s | 2.3 | |
| 27 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 3.5 |
Alloy Composition
| Aluminum (Al), % | 0.2 to 0.5 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0.5 to 1.8 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Boron (B), % | 0 to 0.015 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 |
| Chromium (Cr), % | 20 to 24 | |
| 0 |
| Cobalt (Co), % | 0 to 5.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 0.020 |
| Lanthanum (La), % | 0.0050 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 | |
| 67.1 to 70 |
| Manganese (Mn), % | 0.3 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 1.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 47.5 to 65.2 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.25 to 0.75 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 29.5 to 30.5 |
| Tungsten (W), % | 13 to 15 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |