N06230 Nickel vs. C96700 Copper

N06230 nickel belongs to the nickel alloys classification, while C96700 copper belongs to the copper alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N06230 nickel and the bottom bar is C96700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
140
Elongation at Break, % 38 to 48
10
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 83
53
Tensile Strength: Ultimate (UTS), MPa 620 to 840
1210
Tensile Strength: Yield (Proof), MPa 330 to 400
550

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 990
310
Melting Completion (Liquidus), °C 1370
1170
Melting Onset (Solidus), °C 1300
1110
Specific Heat Capacity, J/kg-K 420
400
Thermal Conductivity, W/m-K 8.9
30
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 85
90
Density, g/cm3 9.5
8.8
Embodied Carbon, kg CO2/kg material 11
9.5
Embodied Energy, MJ/kg 160
140
Embodied Water, L/kg 290
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 330
99
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 380
1080
Stiffness to Weight: Axial, points 12
8.9
Stiffness to Weight: Bending, points 21
20
Strength to Weight: Axial, points 18 to 25
38
Strength to Weight: Bending, points 17 to 21
29
Thermal Diffusivity, mm2/s 2.3
8.5
Thermal Shock Resistance, points 17 to 23
40

Alloy Composition

Aluminum (Al), % 0.2 to 0.5
0
Beryllium (Be), % 0
1.1 to 1.2
Boron (B), % 0 to 0.015
0
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 0 to 5.0
0
Copper (Cu), % 0
62.4 to 68.8
Iron (Fe), % 0 to 3.0
0.4 to 1.0
Lanthanum (La), % 0.0050 to 0.050
0
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0.3 to 1.0
0.4 to 1.0
Molybdenum (Mo), % 1.0 to 3.0
0
Nickel (Ni), % 47.5 to 65.2
29 to 33
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.25 to 0.75
0 to 0.15
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0.15 to 0.35
Tungsten (W), % 13 to 15
0
Zirconium (Zr), % 0
0.15 to 0.35
Residuals, % 0
0 to 0.5