N06250 Nickel vs. C52400 Bronze
N06250 nickel belongs to the nickel alloys classification, while C52400 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N06250 nickel and the bottom bar is C52400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 82 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 450 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 170 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1000 |
| Melting Onset (Solidus), °C | 1440 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 370 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 35 |
| Density, g/cm3 | 8.6 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 3.6 |
| Embodied Energy, MJ/kg | 140 | |
| 58 |
| Embodied Water, L/kg | 270 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 23 | |
| 14 to 28 |
| Strength to Weight: Bending, points | 21 | |
| 15 to 23 |
| Thermal Shock Resistance, points | 19 | |
| 17 to 32 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0 |
| Chromium (Cr), % | 20 to 23 | |
| 0 |
| Copper (Cu), % | 0.25 to 1.3 | |
| 87.8 to 91 |
| Iron (Fe), % | 7.4 to 19.4 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 10.1 to 12 | |
| 0 |
| Nickel (Ni), % | 50 to 54 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.030 to 0.35 |
| Silicon (Si), % | 0 to 0.090 | |
| 0 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 9.0 to 11 |
| Tungsten (W), % | 0.25 to 1.3 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |