N06255 Nickel vs. R60802 Alloy

N06255 nickel belongs to the nickel alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N06255 nickel and the bottom bar is R60802 alloy.

UNS N06255 Nickel Alloy UNS R60802 Zirconium-Tin Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		98

Elongation at Break, %		45
Elongation at Break, %		22

Poisson's Ratio		0.28
Poisson's Ratio		0.34

Shear Modulus, GPa		81
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		660
Tensile Strength: Ultimate (UTS), MPa		430

Tensile Strength: Yield (Proof), MPa		250
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		250

Specific Heat Capacity, J/kg-K		450
Specific Heat Capacity, J/kg-K		270

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		6.0

Otherwise Unclassified Properties

Density, g/cm³		8.5
Density, g/cm³		6.5

Embodied Water, L/kg		270
Embodied Water, L/kg		290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		230
Resilience: Ultimate (Unit Rupture Work), MJ/m³		85

Resilience: Unit (Modulus of Resilience), kJ/m³		150
Resilience: Unit (Modulus of Resilience), kJ/m³		380

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		8.3

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		19

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		53

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0

Chromium (Cr), %		23 to 26
Chromium (Cr), %		0.050 to 0.15

Copper (Cu), %		0 to 1.2
Copper (Cu), %		0

Iron (Fe), %		6.0 to 24
Iron (Fe), %		0.070 to 0.2

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0

Molybdenum (Mo), %		6.0 to 9.0
Molybdenum (Mo), %		0

Nickel (Ni), %		47 to 52
Nickel (Ni), %		0.030 to 0.080

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		1.2 to 1.7

Titanium (Ti), %		0 to 0.69
Titanium (Ti), %		0

Tungsten (W), %		0 to 3.0
Tungsten (W), %		0

Zirconium (Zr), %		0
Zirconium (Zr), %		97.8 to 98.7

Residuals, %		0
Residuals, %		0 to 0.11