N06603 Nickel vs. AWS E410
N06603 nickel belongs to the nickel alloys classification, while AWS E410 belongs to the iron alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N06603 nickel and the bottom bar is AWS E410.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 28 | |
| 23 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 740 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 270 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1450 |
| Melting Onset (Solidus), °C | 1300 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 28 |
| Thermal Expansion, µm/m-K | 14 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 7.5 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 2.0 |
| Embodied Energy, MJ/kg | 120 | |
| 28 |
| Embodied Water, L/kg | 300 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 | |
| 500 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 | |
| 21 |
| Strength to Weight: Bending, points | 22 | |
| 20 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 7.5 |
| Thermal Shock Resistance, points | 20 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 2.4 to 3.0 | |
| 0 |
| Carbon (C), % | 0.2 to 0.4 | |
| 0 to 0.12 |
| Chromium (Cr), % | 24 to 26 | |
| 11 to 13.5 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.75 |
| Iron (Fe), % | 8.0 to 11 | |
| 82.2 to 89 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 57.7 to 65.6 | |
| 0 to 0.7 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.9 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.010 to 0.25 | |
| 0 |
| Yttrium (Y), % | 0.010 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0.010 to 0.1 | |
| 0 |