N06603 Nickel vs. AWS ENiCrMo-4
Both N06603 nickel and AWS ENiCrMo-4 are nickel alloys. They have 78% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is N06603 nickel and the bottom bar is AWS ENiCrMo-4.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 28 | |
| 28 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 740 | |
| 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 320 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1590 |
| Melting Onset (Solidus), °C | 1300 | |
| 1530 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 410 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 70 |
| Density, g/cm3 | 8.2 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 13 |
| Embodied Energy, MJ/kg | 120 | |
| 170 |
| Embodied Water, L/kg | 300 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 25 | |
| 24 |
| Strength to Weight: Bending, points | 22 | |
| 21 |
| Thermal Shock Resistance, points | 20 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 2.4 to 3.0 | |
| 0 |
| Carbon (C), % | 0.2 to 0.4 | |
| 0 to 0.020 |
| Chromium (Cr), % | 24 to 26 | |
| 14.5 to 16.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.5 |
| Iron (Fe), % | 8.0 to 11 | |
| 4.0 to 7.0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 15 to 17 |
| Nickel (Ni), % | 57.7 to 65.6 | |
| 49.9 to 63.5 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.010 to 0.25 | |
| 0 |
| Tungsten (W), % | 0 | |
| 3.0 to 4.5 |
| Vanadium (V), % | 0 | |
| 0 to 0.35 |
| Yttrium (Y), % | 0.010 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0.010 to 0.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |