N06603 Nickel vs. SAE-AISI 1023 Steel

N06603 nickel belongs to the nickel alloys classification, while SAE-AISI 1023 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is N06603 nickel and the bottom bar is SAE-AISI 1023 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 28
17 to 29
Fatigue Strength, MPa 230
180 to 270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 480
280 to 300
Tensile Strength: Ultimate (UTS), MPa 740
430 to 480
Tensile Strength: Yield (Proof), MPa 340
240 to 410

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1340
1460
Melting Onset (Solidus), °C 1300
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 11
53
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 50
1.8
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 8.4
1.4
Embodied Energy, MJ/kg 120
18
Embodied Water, L/kg 300
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
77 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 300
150 to 450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
15 to 17
Strength to Weight: Bending, points 22
16 to 17
Thermal Diffusivity, mm2/s 2.9
14
Thermal Shock Resistance, points 20
14 to 15

Alloy Composition

Aluminum (Al), % 2.4 to 3.0
0
Carbon (C), % 0.2 to 0.4
0.2 to 0.25
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 8.0 to 11
99.06 to 99.5
Manganese (Mn), % 0 to 0.15
0.3 to 0.6
Nickel (Ni), % 57.7 to 65.6
0
Phosphorus (P), % 0 to 0.2
0 to 0.040
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0 to 0.050
Titanium (Ti), % 0.010 to 0.25
0
Yttrium (Y), % 0.010 to 0.15
0
Zinc (Zn), % 0.010 to 0.1
0