N06603 Nickel vs. SAE-AISI 1025 Steel
N06603 nickel belongs to the nickel alloys classification, while SAE-AISI 1025 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is N06603 nickel and the bottom bar is SAE-AISI 1025 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 28 | |
| 17 to 28 |
| Fatigue Strength, MPa | 230 | |
| 190 to 280 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 480 | |
| 290 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 740 | |
| 450 to 500 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 250 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 400 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1460 |
| Melting Onset (Solidus), °C | 1300 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 52 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 1.8 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 120 | |
| 18 |
| Embodied Water, L/kg | 300 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 80 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 | |
| 170 to 470 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 25 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 22 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 14 |
| Thermal Shock Resistance, points | 20 | |
| 14 to 16 |
Alloy Composition
| Aluminum (Al), % | 2.4 to 3.0 | |
| 0 |
| Carbon (C), % | 0.2 to 0.4 | |
| 0.22 to 0.28 |
| Chromium (Cr), % | 24 to 26 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 8.0 to 11 | |
| 99.03 to 99.48 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 57.7 to 65.6 | |
| 0 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0.010 to 0.25 | |
| 0 |
| Yttrium (Y), % | 0.010 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0.010 to 0.1 | |
| 0 |