N06650 nickel belongs to the nickel alloys classification, while AWS BAg-10 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06650 nickel and the bottom bar is AWS BAg-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
82
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 82
30
Tensile Strength: Ultimate (UTS), MPa 900
140

Thermal Properties

Latent Heat of Fusion, J/g 320
130
Melting Completion (Liquidus), °C 1500
740
Melting Onset (Solidus), °C 1450
690
Specific Heat Capacity, J/kg-K 440
280
Thermal Expansion, µm/m-K 12
20

Otherwise Unclassified Properties

Density, g/cm3 8.6
9.8

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 29
4.0
Strength to Weight: Bending, points 24
6.1
Thermal Shock Resistance, points 24
6.2

Alloy Composition

Aluminum (Al), % 0.050 to 0.5
0
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 21
0
Cobalt (Co), % 0 to 1.0
0
Copper (Cu), % 0 to 0.3
19 to 21
Iron (Fe), % 12 to 16
0
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 9.5 to 12.5
0
Nickel (Ni), % 44.4 to 58.9
0
Niobium (Nb), % 0.050 to 0.5
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
69 to 71
Sulfur (S), % 0 to 0.010
0
Tungsten (W), % 0.5 to 2.5
0
Zinc (Zn), % 0
8.0 to 12
Residuals, % 0
0 to 0.15