N06650 Nickel vs. AWS ENiCrCoMo-1

Both N06650 nickel and AWS ENiCrCoMo-1 are nickel alloys. They have 83% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N06650 nickel and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Elongation at Break, % 50
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 82
82
Tensile Strength: Ultimate (UTS), MPa 900
710

Thermal Properties

Latent Heat of Fusion, J/g 320
330
Melting Completion (Liquidus), °C 1500
1430
Melting Onset (Solidus), °C 1450
1380
Specific Heat Capacity, J/kg-K 440
440
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 60
75
Density, g/cm3 8.6
8.5
Embodied Carbon, kg CO2/kg material 10
11
Embodied Energy, MJ/kg 140
140
Embodied Water, L/kg 270
340

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 29
23
Strength to Weight: Bending, points 24
21
Thermal Shock Resistance, points 24
19

Alloy Composition

Aluminum (Al), % 0.050 to 0.5
0
Carbon (C), % 0 to 0.030
0.050 to 0.15
Chromium (Cr), % 19 to 21
21 to 26
Cobalt (Co), % 0 to 1.0
9.0 to 15
Copper (Cu), % 0 to 0.3
0 to 0.5
Iron (Fe), % 12 to 16
0 to 5.0
Manganese (Mn), % 0 to 0.5
0.3 to 2.5
Molybdenum (Mo), % 9.5 to 12.5
8.0 to 10
Nickel (Ni), % 44.4 to 58.9
38.6 to 61.7
Niobium (Nb), % 0.050 to 0.5
0 to 1.0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.010
0 to 0.015
Tungsten (W), % 0.5 to 2.5
0
Residuals, % 0
0 to 0.5