N06650 Nickel vs. EN 1.4057 Stainless Steel

N06650 nickel belongs to the nickel alloys classification, while EN 1.4057 stainless steel belongs to the iron alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N06650 nickel and the bottom bar is EN 1.4057 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 50
11 to 17
Fatigue Strength, MPa 420
320 to 430
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 82
77
Shear Strength, MPa 640
520 to 580
Tensile Strength: Ultimate (UTS), MPa 900
840 to 980
Tensile Strength: Yield (Proof), MPa 460
530 to 790

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Mechanical, °C 980
850
Melting Completion (Liquidus), °C 1500
1440
Melting Onset (Solidus), °C 1450
1390
Specific Heat Capacity, J/kg-K 440
480
Thermal Expansion, µm/m-K 12
10

Otherwise Unclassified Properties

Base Metal Price, % relative 60
9.5
Density, g/cm3 8.6
7.7
Embodied Carbon, kg CO2/kg material 10
2.2
Embodied Energy, MJ/kg 140
32
Embodied Water, L/kg 270
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 380
96 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 490
700 to 1610
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 29
30 to 35
Strength to Weight: Bending, points 24
26 to 28
Thermal Shock Resistance, points 24
30 to 35

Alloy Composition

Aluminum (Al), % 0.050 to 0.5
0
Carbon (C), % 0 to 0.030
0.12 to 0.22
Chromium (Cr), % 19 to 21
15 to 17
Cobalt (Co), % 0 to 1.0
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 12 to 16
77.7 to 83.4
Manganese (Mn), % 0 to 0.5
0 to 1.5
Molybdenum (Mo), % 9.5 to 12.5
0
Nickel (Ni), % 44.4 to 58.9
1.5 to 2.5
Niobium (Nb), % 0.050 to 0.5
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Tungsten (W), % 0.5 to 2.5
0