N06650 Nickel vs. EN 1.5503 Steel
N06650 nickel belongs to the nickel alloys classification, while EN 1.5503 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N06650 nickel and the bottom bar is EN 1.5503 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 50 | |
| 12 to 17 |
| Fatigue Strength, MPa | 420 | |
| 180 to 280 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 82 | |
| 73 |
| Shear Strength, MPa | 640 | |
| 270 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 900 | |
| 400 to 520 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 270 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 400 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1460 |
| Melting Onset (Solidus), °C | 1450 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.8 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 1.4 |
| Embodied Energy, MJ/kg | 140 | |
| 18 |
| Embodied Water, L/kg | 270 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 380 | |
| 41 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 200 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 29 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 24 | |
| 15 to 18 |
| Thermal Shock Resistance, points | 24 | |
| 12 to 15 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.5 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.030 | |
| 0.16 to 0.2 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 12 to 16 | |
| 98.4 to 99.239 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 9.5 to 12.5 | |
| 0 |
| Nickel (Ni), % | 44.4 to 58.9 | |
| 0 |
| Niobium (Nb), % | 0.050 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0.050 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.025 |
| Tungsten (W), % | 0.5 to 2.5 | |
| 0 |