N06920 Nickel vs. ASTM A182 Grade F3V
N06920 nickel belongs to the nickel alloys classification, while ASTM A182 grade F3V belongs to the iron alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is N06920 nickel and the bottom bar is ASTM A182 grade F3V.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 39 | |
| 20 |
| Fatigue Strength, MPa | 220 | |
| 330 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 82 | |
| 74 |
| Shear Strength, MPa | 500 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 470 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1470 |
| Melting Onset (Solidus), °C | 1440 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 39 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 4.2 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 2.3 |
| Embodied Energy, MJ/kg | 130 | |
| 33 |
| Embodied Water, L/kg | 270 | |
| 63 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 230 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 590 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 23 |
| Strength to Weight: Bending, points | 21 | |
| 21 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 10 |
| Thermal Shock Resistance, points | 19 | |
| 19 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.0010 to 0.0030 |
| Carbon (C), % | 0 to 0.030 | |
| 0.050 to 0.18 |
| Chromium (Cr), % | 20.5 to 23 | |
| 2.8 to 3.2 |
| Cobalt (Co), % | 0 to 5.0 | |
| 0 |
| Iron (Fe), % | 17 to 20 | |
| 94.4 to 95.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 36.9 to 53.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0.015 to 0.035 |
| Tungsten (W), % | 1.0 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |