N06920 Nickel vs. Nickel 625

Both N06920 nickel and nickel 625 are nickel alloys. They have 79% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is N06920 nickel and the bottom bar is nickel 625.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 39
33 to 34
Fatigue Strength, MPa 220
240 to 320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 82
79
Shear Strength, MPa 500
530 to 600
Tensile Strength: Ultimate (UTS), MPa 730
790 to 910
Tensile Strength: Yield (Proof), MPa 270
320 to 450

Thermal Properties

Latent Heat of Fusion, J/g 320
330
Maximum Temperature: Mechanical, °C 990
980
Melting Completion (Liquidus), °C 1500
1350
Melting Onset (Solidus), °C 1440
1290
Specific Heat Capacity, J/kg-K 440
440
Thermal Conductivity, W/m-K 11
11
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 55
80
Density, g/cm3 8.6
8.6
Embodied Carbon, kg CO2/kg material 9.4
14
Embodied Energy, MJ/kg 130
190
Embodied Water, L/kg 270
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
220 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 180
260 to 490
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 24
26 to 29
Strength to Weight: Bending, points 21
22 to 24
Thermal Diffusivity, mm2/s 2.8
2.9
Thermal Shock Resistance, points 19
22 to 25

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 20.5 to 23
20 to 23
Cobalt (Co), % 0 to 5.0
0 to 1.0
Iron (Fe), % 17 to 20
0 to 5.0
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 8.0 to 10
8.0 to 10
Nickel (Ni), % 36.9 to 53.5
58 to 68.9
Niobium (Nb), % 0
3.2 to 4.2
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.4
Tungsten (W), % 1.0 to 3.0
0