N06985 nickel belongs to the nickel alloys classification, while AWS BAg-8 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is N06985 nickel and the bottom bar is AWS BAg-8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
84
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 80
31
Tensile Strength: Ultimate (UTS), MPa 690
150

Thermal Properties

Latent Heat of Fusion, J/g 320
140
Melting Completion (Liquidus), °C 1350
780
Melting Onset (Solidus), °C 1260
780
Specific Heat Capacity, J/kg-K 450
280
Thermal Expansion, µm/m-K 15
19

Otherwise Unclassified Properties

Density, g/cm3 8.4
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 23
14
Strength to Weight: Axial, points 23
4.1
Strength to Weight: Bending, points 21
6.2
Thermal Shock Resistance, points 16
6.7

Alloy Composition

Carbon (C), % 0 to 0.015
0
Chromium (Cr), % 21 to 23.5
0
Cobalt (Co), % 0 to 5.0
0
Copper (Cu), % 1.5 to 2.5
26.9 to 29
Iron (Fe), % 18 to 21
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 6.0 to 8.0
0
Nickel (Ni), % 35.9 to 53.5
0
Niobium (Nb), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
71 to 73
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 0 to 1.5
0
Residuals, % 0
0 to 0.15