N07041 Nickel vs. AISI 201L Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 201L stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 201L stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 22 to 46 |
| Fatigue Strength, MPa | 540 | |
| 270 to 530 |
| Shear Strength, MPa | 850 | |
| 520 to 660 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 740 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 290 to 790 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 210 to 300 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 220 to 1570 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 27 to 37 |
| Strength to Weight: Bending, points | 34 | |
| 24 to 30 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 4.0 |
| Thermal Shock Resistance, points | 38 | |
| 16 to 23 |