N07041 Nickel vs. AISI 205 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while AISI 205 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 205 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
11 to 51
Fatigue Strength, MPa 540
410 to 640
Shear Strength, MPa 850
560 to 850
Tensile Strength: Ultimate (UTS), MPa 1400
800 to 1430
Tensile Strength: Yield (Proof), MPa 1050
450 to 1100

Thermal Properties

Melting Onset (Solidus), °C 1320
1340
Specific Heat Capacity, J/kg-K 450
480
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.6

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
150 to 430
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
510 to 3060
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 47
29 to 52
Strength to Weight: Bending, points 34
25 to 37
Thermal Shock Resistance, points 38
16 to 29