N07041 Nickel vs. AISI 301LN Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 301LN stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 301LN stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 | |
200 |
Elongation at Break, % | 14 | |
23 to 51 |
Fatigue Strength, MPa | 540 | |
270 to 520 |
Shear Strength, MPa | 850 | |
450 to 670 |
Tensile Strength: Ultimate (UTS), MPa | 1400 | |
630 to 1060 |
Tensile Strength: Yield (Proof), MPa | 1050 | |
270 to 770 |
Thermal Properties
Melting Onset (Solidus), °C | 1320 | |
1380 |
Specific Heat Capacity, J/kg-K | 450 | |
480 |
Thermal Conductivity, W/m-K | 11 | |
15 |
Thermal Expansion, µm/m-K | 12 | |
16 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
220 to 290 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
180 to 1520 |
Stiffness to Weight: Axial, points | 15 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 47 | |
22 to 38 |
Strength to Weight: Bending, points | 34 | |
21 to 30 |
Thermal Diffusivity, mm2/s | 3.0 | |
4.0 |
Thermal Shock Resistance, points | 38 | |
14 to 24 |