N07041 Nickel vs. AISI 302 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 302 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 302 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 4.5 to 46 |
| Fatigue Strength, MPa | 540 | |
| 210 to 520 |
| Shear Strength, MPa | 850 | |
| 400 to 830 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 580 to 1430 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 230 to 1100 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 59 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 140 to 3070 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 21 to 51 |
| Strength to Weight: Bending, points | 34 | |
| 20 to 36 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 4.4 |
| Thermal Shock Resistance, points | 38 | |
| 12 to 31 |