N07041 Nickel vs. AISI 422 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 422 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 422 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 15 to 17 |
| Fatigue Strength, MPa | 540 | |
| 410 to 500 |
| Shear Strength, MPa | 850 | |
| 560 to 660 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 910 to 1080 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 670 to 870 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 24 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 1140 to 1910 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 32 to 38 |
| Strength to Weight: Bending, points | 34 | |
| 26 to 30 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 6.4 |
| Thermal Shock Resistance, points | 38 | |
| 33 to 39 |