N07041 Nickel vs. ASTM A148 Cast Steel
N07041 nickel belongs to the nickel alloys classification, while ASTM A148 cast steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is ASTM A148 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 5.7 to 25 |
| Fatigue Strength, MPa | 540 | |
| 280 to 670 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 630 to 1300 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 390 to 1160 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 37 to 47 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 400 to 3570 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 22 to 46 |
| Strength to Weight: Bending, points | 34 | |
| 21 to 34 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 9.9 to 13 |
| Thermal Shock Resistance, points | 38 | |
| 18 to 38 |