N07041 Nickel vs. Ductile Cast Iron
N07041 nickel belongs to the nickel alloys classification, while ductile cast iron belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is ductile cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 170 to 180 |
| Elongation at Break, % | 14 | |
| 2.1 to 20 |
| Shear Strength, MPa | 850 | |
| 420 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 460 to 920 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 310 to 670 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 490 |
| Thermal Conductivity, W/m-K | 11 | |
| 31 to 36 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.1 to 7.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 17 to 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 280 to 1330 |
| Stiffness to Weight: Axial, points | 15 | |
| 12 to 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 to 26 |
| Strength to Weight: Axial, points | 47 | |
| 17 to 35 |
| Strength to Weight: Bending, points | 34 | |
| 18 to 29 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 8.9 to 10 |
| Thermal Shock Resistance, points | 38 | |
| 17 to 35 |