N07041 Nickel vs. EN 1.0303 Steel
N07041 nickel belongs to the nickel alloys classification, while EN 1.0303 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.0303 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 12 to 25 |
| Fatigue Strength, MPa | 540 | |
| 150 to 230 |
| Shear Strength, MPa | 850 | |
| 220 to 260 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 290 to 410 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 200 to 320 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 53 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 30 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 110 to 270 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 10 to 15 |
| Strength to Weight: Bending, points | 34 | |
| 12 to 16 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 14 |
| Thermal Shock Resistance, points | 38 | |
| 9.2 to 13 |