MakeItFrom.com
Menu (ESC)

N07041 Nickel vs. EN 1.0434 Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.0434 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.0434 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 14
12 to 28
Fatigue Strength, MPa 540
190 to 300
Shear Strength, MPa 850
280 to 330
Tensile Strength: Ultimate (UTS), MPa 1400
390 to 540
Tensile Strength: Yield (Proof), MPa 1050
250 to 450

Thermal Properties

Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
52
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
39 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
170 to 540
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 47
14 to 19
Strength to Weight: Bending, points 34
15 to 19
Thermal Diffusivity, mm2/s 3.0
14
Thermal Shock Resistance, points 38
12 to 17