N07041 Nickel vs. EN 1.4057 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.4057 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4057 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
11 to 17
Fatigue Strength, MPa 540
320 to 430
Shear Strength, MPa 850
520 to 580
Tensile Strength: Ultimate (UTS), MPa 1400
840 to 980
Tensile Strength: Yield (Proof), MPa 1050
530 to 790

Thermal Properties

Melting Onset (Solidus), °C 1320
1390
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 11
25
Thermal Expansion, µm/m-K 12
10

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.7

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
96 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
700 to 1610
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
30 to 35
Strength to Weight: Bending, points 34
26 to 28
Thermal Diffusivity, mm2/s 3.0
6.7
Thermal Shock Resistance, points 38
30 to 35