N07041 Nickel vs. EN 1.4378 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.4378 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4378 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
14 to 34
Fatigue Strength, MPa 540
340 to 550
Shear Strength, MPa 850
510 to 680
Tensile Strength: Ultimate (UTS), MPa 1400
760 to 1130
Tensile Strength: Yield (Proof), MPa 1050
430 to 970

Thermal Properties

Melting Onset (Solidus), °C 1320
1350
Specific Heat Capacity, J/kg-K 450
480
Thermal Expansion, µm/m-K 12
17

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.6

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
150 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
470 to 2370
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
28 to 41
Strength to Weight: Bending, points 34
24 to 31
Thermal Shock Resistance, points 38
16 to 23