N07041 nickel belongs to the nickel alloys classification, while EN 1.4401 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4401 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
14 to 40
Fatigue Strength, MPa 540
200 to 320
Shear Strength, MPa 850
410 to 550
Tensile Strength: Ultimate (UTS), MPa 1400
600 to 900
Tensile Strength: Yield (Proof), MPa 1050
230 to 570

Thermal Properties

Melting Onset (Solidus), °C 1320
1400
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
130 to 800
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
21 to 32
Strength to Weight: Bending, points 34
20 to 26
Thermal Diffusivity, mm2/s 3.0
4.0
Thermal Shock Resistance, points 38
13 to 20