N07041 Nickel vs. EN 1.4415 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.4415 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
17 to 20
Fatigue Strength, MPa 540
470 to 510
Shear Strength, MPa 850
520 to 570
Tensile Strength: Ultimate (UTS), MPa 1400
830 to 930
Tensile Strength: Yield (Proof), MPa 1050
730 to 840

Thermal Properties

Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
19
Thermal Expansion, µm/m-K 12
9.9

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
150 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
1350 to 1790
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
29 to 33
Strength to Weight: Bending, points 34
25 to 27
Thermal Diffusivity, mm2/s 3.0
5.1
Thermal Shock Resistance, points 38
30 to 34